It is the aim of the present book to make the reader familiar with the application of a model developed by Andries Miedema which opened completely new perspectives in materials science. For example, a result that was obtained by a one-month run on a Cray 1 supercomputer turned out to be only a few kilo Joules different from the outcome by Miedema?s model, obtained within a few minutes by use of a pocket calculator.
Autoren/Hrsg.
Weitere Infos & Material
1. The Macroscopic Atom Model; Three Fundamentalquantities2. Estimateof the Chemical Part of the Formation Enthalpy of a Dilute Random Solidsolution3. Estimate of the Formation Enthalpy of Anintermetallic Compound4. Volumeeffects upon Alloying5. Solid Solubility6. Some Thermodynamics7. The Importance of the Structural Term8. Surfaceenergy and Enthalpy of Atomisation1. Application to the Formation and Cohesiveenthalpies of Intermetallic Compounds2. Application to Solid Solubility3. Formation Enthalpy of Concentrated Solidsolutions4. Formationenthalpy of Amorphous Alloys5. Comparison of the Formation Enthalpy of Theamorphous Alloy with the Formation Enthalpy of the Solid Solution6. Formationenthalpy of Ternary Alloys7. Application to Volume Effects upon Alloying8. Applicationto the Heat of Atomisation. 9. Vacancyformation Enthalpies in Pure Metals and Alloys.10. Anti-Site Disorder in Ordered Compounds11. Vacancy Formation in Ordered Intermetallics12. Anti-Site Disorder versus Triple-Defect Disorderand Schottky Defects F.13. Crystallisation Temperature of Amorphous Alloys14. Metal Surfaces