Advances in Fracture and Damage Mechanics XIII

Erscheinungsjahr 2015
ISBN: 978-3-03795-931-2
Verlag: Trans Tech Publications

Sonstiges, Englisch, Band Volume 627, 510 Seiten, Format (B × H): 125 mm x 142 mm, Gewicht: 200 g

Reihe: Key Engineering Materials

Collection of selected, peer reviewed papers from the 13th International Conference on Fracture and Damage Mechanics (FDM 2014), September 23-25, 2014, S?o Miguel Island, Azores, Portugal.

Autoren/Hrsg.

Alfaiate, J.

M.H.Aliabadi, Ferri

Fachgebiete

• Technische Wissenschaften Maschinenbau | Werkstoffkunde Technische Mechanik | Werkstoffkunde Werkstoffkunde, Materialwissenschaft: Forschungsmethoden
• Technische Wissenschaften Maschinenbau | Werkstoffkunde Technische Mechanik | Werkstoffkunde Festigkeitslehre, Belastbarkeit
• Technische Wissenschaften Maschinenbau | Werkstoffkunde Technische Mechanik | Werkstoffkunde Werkstoffprüfung

Inhaltsverzeichnis

Lamb-Wave Based Damage Detection in Anisotropic Composite PlatesAnalysis of 3D Planar Crack Problems by Body Force MethodLong Life Fatigue Behavior of Shot Peened SteelsA Finite Fracture Mechanics Model for the Prediction of the Notched Response and Large Damage Capability of Composite LaminatesLow-Cost System to Evaluate Impact Localization in Composite PlatesModeling Delamination Growth in Composite Panels Subjected to Fatigue LoadDefinition of a Constitutive Material Model for Progressive Failure Analysis of Composite LaminatesRound Timber Bolted Joints with Steel Plates under Static and Cyclic LoadingA Multiscale Approach to Polycrystalline Materials Damage and FailureA Multi-Scale Scheme for Modelling Fracture under Dynamic Loading ConditionsEstimation of the Crack Behaviour in the Compressive Layer of the Alumina-Zirconia Ceramic LaminateFatigue Life Assessment of Self-Expandable NiTi StentModelling Mixed-Mode Fracture Using an Energy-Based Damage ModelMulti-Scale Mechanical Property Characterisation of Quasi-Brittle Filter GraphiteFE Analysis of Functionally Graded Material Plate during Debonding Case with Different Boundary ConditionsOptimized Design of Strengthening Structure with Hat-Shaped Cross-Section by Carrying out Buckling TestHigh Magnification Studies of Fatigue Crack PropagationFracture Behavior of Notched Round Bars Made of Gray Cast Iron Subjected to TorsionPolymethylmethacrylate Data from U-Notched Specimens and V-Notches with End Holes: A Synthesis by Means of Local EnergyHigh Temperature Fatigue Tests of a Cu-Be Alloy and Synthesis in Terms of Linear Elastic Strain Energy DensityFatigue Behaviour of DLC Coated Al 7075-T6 Alloy in an Aggressive MixtureGaussian Specimens for Gigacycle Fatigue Tests: Evaluation of Temperature IncrementVibrational and Inertial Effects of Methane Hydrates in the Failure of a PipelineEvaluation by FEM of the Influence of the Preheating and Post-Heating Treatments on Residual Stresses in WeldingFatigue Behaviour of Full Scale Flat Stiffened Aeronautic PanelsNumerical Study of a Plate with a Pre-Cracked Circular NotchNumerical Simulation and Experimental Investigation of Damage Behaviour on Al6061 Laser Welded JointsFlexural Property and Mode I Interlaminar Fracture Toughness of Plain Woven Carbon Fiber Reinforced Plastics after Water Absorption and FreezingEffect of Acid Treatment on Mechanical Performance of Polyvinyl Alcohol/Halloysite NanocompositesA Theory for Mathematical Framework of Fatigue Damage on S-N PlaneTopology Optimization of Geometrically Non-Linear Structures Using Iso-XFEM MethodFracture Mechanisms in High-Cycle Fatigue of Selective Laser Melted Ti-6Al-4VInvestigation of Residual Stresses in Selective Laser MeltingExperimental Evaluation of Fatigue Resistance of ETG?88 and C45+C Steels Considering Stress Concentrators and Scale FactorFatigue and Fracture Resistance of an Aircraft Landing Gear Steels V-ROL N and VIP P-ROL N Heat Treated to Lower Strength LimitThe Effect of Specimen Size on the Determination of Residual Stress in Polymer Pipe WallDescription of Fatigue Crack Propagation under Mixed-Mode II+III in Terms of J-IntegralFatigue Crack Propagation in Hydrogen Gas in Low Alloyed SteelFatigue Crack Propagation in Thin Wires of Ultra-High Strength SteelHydrogen-Assisted Rolling-Contact Fatigue of Wind Turbines BearingsInelastic Dynamic and Non-Linear Static Seismic Performance of a Building with RC Walls that Collapsed in the Chile?s Earthquake of February 2010 and a Building with RC Concrete Frame Designed in the Mexico CityInfluence of the V-Notch Opening Angle on Critical Applied Force Values for the Crack Initiation from the Sharp V-NotchInfluence of Annealing Process on Crystallinity of Glass Fiber Reinforced Easily Degradable PLA CompositesEffect of High Temperature on Fiber/Matrix Interfacial Properties for Carbon Fiber/Polyphenylenesulfide Model CompositesEffect of Hot Water Environment on Tensile Fracture Properties of Carbon Fiber Reinforced Polyoxamide CompositesStability Evaluation of Gearbox for Independent Wheel Drive under Various Driving ModeTime to Failure Size Effect for Tensile Creep SpecimensCorrosion Resistance Testing of the Galvanized Sheet Metal Braze Welding JointsFatigue Behaviour of Al 6082-T6 Friction Stir Welded Tubular Joints under Torsional LoadingThe Effect of Soil Load on Fracture Behaviour of Three-Layer Polymer Pipe for Non-Pressurised ApplicationsHigh-Cycle Fatigue Damage of Oxygen-Free and Deoxidized-Phosphorous Copper Processed by Equal Channel Angular PressingLong Term High-Temperature Environmental Effect on Impact Toughness in Austenitic AlloysThe Importance of Micro-Crack Evolution under Oxidation/Creep Conditions in Component Failure Life PredictionsAutomation Using Matrix Switch for Piezoelectric Actuator/Sensor Based Structural Health MonitoringLocalization of Barely Visible Impact Damage (BVID) in Composite PlatesFracture in the Single Cantilever Beam Test with Large Scale BridgingIntersection of Interface Crack Front with Free EdgeFatigue Strength Simulation and Prediction of a Turbine BladeStudy of Nanostructured Composites Using the Sclerometry MethodValidity of the Finite Fracture Mechanics Based Asymptotic Analysis for Predictions of Crack Deflection in Thin Layers of Ceramic LaminatesCharacterization of Local Deformation in Welded Joints Using a Combined Experimental and Numerical ApproachThe Effect of Anchorage Strength with Anchorage Capacity in Flat PlateExperimental Study on Pounding between Structures during Damaging EarthquakesHigh Speed Fracture Phenomena by Underwater Shockwave of Explosive Energy and Large Current Pulse in Glass ContainerGun Bullet Collision and Penetration Problem in Polycarbonate BoardDesign/Manufacturing System for Composite Ankle Foot OrthosisFatigue Characteristics of Nonferrous Bolts at Elevated TemperatureCrack Analysis in Piezoelectric SemiconductorsEvaluation of Crack Tip Stress Field Using Combination of Advanced Implementation of Over-Deterministic Method and FE AnalysisNumerical Simulation of Modified Compact Tension Test Depicting of Experimental Measurement by ARAMISWedge Splitting Test of Foam Concrete Specimens: Calibration CurvesNumerical Simulation for Mechanical Behavior of Carbon Black Filled Rubber Composites Based on Cubic Representative Volume ElementNumerical Analysis of Three-Dimensional Semi-Elliptical Interfacial Cracks Subjected to Indentation LoadThermal Cycling Life of Porous Ceramic Coatings Subjected to Thermal Gradient and Coolant PressureDeviations of Microcrack during Propagation in Thin Films of Austenitic Steel and Accompanying Accommodative ProcessesComparison of Artificial Neural Networks and the Transfer Function Method for Force Reconstruction in Curved Composite PlatesFatigue Crack Growth Rates and Tensile Strength of Titanium Produced by Means of Selective Laser MeltingComparison of Full Field and Single Inclusion Approaches to Homogenization of Composites with Non-Ellipsoidal PoresApplication of Acoustic Emission for Identification of Differences in Fatigue Damage of Selected Materials for Power PlantsWork of Fracture due to Compressive Component of Loading in Wedge Splitting Test on Quasi-Brittle Cementitious SpecimensPrediction of Corrosion Processes on Weathering Steel BridgesAnalytical 1D Model of Delamination Development and Strength of Layered Composite Beam in Post-BucklingMicroindentation Test Modelling in the Silicon Nitride Ceramics by Application of the Cohesive Zone ApproachComparative Study on the Fatigue Behaviour of SCC and VCReview of FE-Based Fatigue Evaluation Methods for the Rib to Floorbeam Welds in Orthotropic Bridge DecksAn Integrated Creep-Fatigue Theory for Material Damage ModelingStress Analysis of Cracked MMCs with Lamellar MicrostructureContinuum Approach to Computational Multi-Scale Modeling of FractureCorrelation of Dent Depth to Maximum Contact Force and Damage of Composite LaminatesMeshless Approaches for Fracture with Nonlocal ElasticityInvestigation of the Cracking Behaviors by Indentation Based on an In Situ ObservationDeformation-Induced Dynamic Precipitation during Creep in Magnesium-Tin AlloysMechanical Properties of Concrete Produced with Wastepaper for Application of Construction MaterialsPoint Load Effect Determination for Different Pressure Pipe SDR SeriesA Technique for Detection and Sizing of Cracks on Plate Structures Using Piezoelectric Transducer NetworksSecond-Order Computational Homogenization Scheme Preserving Microlevel C1 ContinuityThe Relationship of Compressive Strength and Tensile Strength of High Performance ConcreteOptimized Ultra High Performance Fiber Reinforced Concrete Mixture with Intensified Volumetric StabilityEffect of Area Ratio of Coarse Aggregate on Erosion Resistance of Offshore Concrete StructureInvestigation on Compressive Strength after Impact Damage of Carbon/Epoxy LaminateEffect of Mineral Admixture on Modulus of Elasticity in High Performance Concrete under Hot Weather ConditionA Study on the Fatigue Test of Truck Materials for Railway VehiclesA Study on the Safety of Carbody for Railway VehiclesA Development of Innovative Slip-Form System for Concrete PylonsFatigue Behavior of Extruded Mg-Al-Ca-Mn Alloy with T6 Treatment at Elevated TemperatureContact State Investigation of a Three-Point Bend Specimen Using Numerical MethodsAn Experimental Evaluation for Four Multiaxial Fatigue ApproachesVery High Plastic Strain Zones in 304 Stainless Steel Small Punch Specimen Loaded at RT by Martensite Formation and Recrystallization TechniqueComparison between Subjective and Objective Measurement of SlipperinessMicro-Computed Tomography Image Based Numerical Elastic Homogenization of MMCsFibre Concrete Foundation Slab Experiment and FEM AnalysisInfluence of Cold Weather on Compressive Strength in High Performance with Silica FumeThe Behavior of Pseudo Strain-Hardening Cementitious Composite (PSH2C) Using Synthetic Fibers under Uniaxial Tensile LoadingA Boundary Element Method for Structural ReliabilitySimulations of Bending Experiments of Concrete Beams by Stochastic Discrete ModelEvaluation of Slip Resistance of Safety Footwear Using Novel EquipmentApplication of the Radial Integration Method into Dynamic Formulation of Anisotropic Shallow Shells Using Boundary Element MethodInfluence of Different Crack Propagation Rate Descriptions on the Residual Fatigue Lifetime of Railway AxlesNumerical Analysis about the Strength of Jointed Rock under Hydrodynamic PressureInvestigations on Direct Shear Tests and PFC2D Numerical Simulations of Rock-Like Materials with a Hole and Prefabricated Cracks