Kasl | Contribution of Metallography to Production Problem Solutions | Buch | 978-3-0357-2694-7 | sack.de

Buch, Englisch, 206 Seiten, Format (B × H): 170 mm x 240 mm, Gewicht: 490 g

Kasl

Contribution of Metallography to Production Problem Solutions


Buch, Englisch, 206 Seiten, Format (B × H): 170 mm x 240 mm, Gewicht: 490 g

ISBN: 978-3-0357-2694-7
Verlag: Trans Tech Publications

This book contains selected contributions presented at the 15th conference “Contribution of Metallography to Production Problem Solutions” held on 21 – 23 September 2021 in Mariánské Lázne, Czech Republic. The conference was focused on the application of metallography in industrial practice - for the solution of production problems, elucidation of premature failure of machine components and constructions during service, breakdowns or accidents. In addition, some results of new research projects which could improve manufacturing technology or the quality of machine products are presented. Individual papers deal with failure causes and fracture mechanism, insufficient material properties and incorrect function of the components. Using metallographic analyses, which include light and electron microscopy, spectroscopic methods, and physical methods for the detection of defects, material structures are investigated. Results are correlated with material properties, and recommendations for production improvement are given.
Kasl Contribution of Metallography to Production Problem Solutions jetzt bestellen!

Autoren/Hrsg.

Kasl, Josef

Fachgebiete

Weitere Infos & Material

Preface
Chapter 1: Technological Research
Surface Modification of Alumina Particles to Enhance Bonding Properties with Rubber and Resin in Grinding Tools
Stabilizing the Microstructure of Additively Manufactured Low-C Co-28Cr-6Mo Alloy
Production and Application of Magnesium Alloys Castings
Correlating the Microstructure with the Mechanical Behaviour of Titanium Structures Produced by Robotic Assisted Deposition
Hardening of Rail Vehicle Axles
Tribotests of Valve Seats Made of ADI and Q - Cryo Cast Iron with Spheroidal Graphite
Interaction of AZ91 Magnesium Alloy with Ceramic Shell during Investment Casting
Microstructure of Mo-La2O3 Composite Powder Prepared Using Two Different High Energy Ball Milling Systems
Structure and Mechanical Properties of Welded Joints of Large Steel Forgings for Nuclear Power Plants of MIR 1200 Type
The Evaluation of Ti-24Nb-8Ta-4Sn Alloy Prepared by 3D Printing
Influence of Forging Parameters on Microstructure and Properties of En AW-6082 Alloy
Metallographic Evaluation of Ni-Cr Cold Spray Layers on the Tube
Laser Surface Hardening of Graphite Cast Iron
Chapter 2: Materials Degradation
Damage and Fracture in Creep of a Cast B1914 Superalloy
Influence of Processing Technology on Creep Damage of Ultrafine-Grained Titanium
Effect of Graphite on Residual Lifetime of Superheater Tubes Made of Steel 16Mo3 after Creep Exposure

In Vitro Corrosion Study of Selected Laser Melted WE43 Magnesium Alloy in Hank ´s Balanced Salt Solution
Creep Damage in Steam Pipelines and the Use of Metallography in Verifying the Possibilities of Testing
Chapter 3: Failure Analysis
Causes of Injection Mould Insert Block Damage
Analysis of the Causes of Shaft Damage
Analysis of Cracked Rail of the Crane of Type A120
Analysis of the Causes of Failure and Material Analysis of Components of the Screw Conveyor of a Coal Boiler for Steam Production
Chapter 4: Production Defects
Castings Defect Analyses
Analysis of the Causes of Increased Reject Rate in Connecting Rod Production
Analysis of Defects Associated with Manufacturing Keys for Brass Musical Instruments
Analysis of a Damaged Drill Made from Hs 2-9-1-8 Steel
Chapter 5: Testing and Examination Methods
Application of Metallographic Investigation in Development of Sub-Sized Specimen Testing Techniques
Characteristics of Metallographic Preparation of Heat Exchanger Austenitic Stainless Steels
Replicas Application in Non-Destructive Testing

Ihre Fragen, Wünsche oder Anmerkungen
Vorname*
Nachname*
Ihre E-Mail-Adresse*
Kundennr.
Ihre Nachricht*
Lediglich mit * gekennzeichnete Felder sind Pflichtfelder.
Wenn Sie die im Kontaktformular eingegebenen Daten durch Klick auf den nachfolgenden Button übersenden, erklären Sie sich damit einverstanden, dass wir Ihr Angaben für die Beantwortung Ihrer Anfrage verwenden. Selbstverständlich werden Ihre Daten vertraulich behandelt und nicht an Dritte weitergegeben. Sie können der Verwendung Ihrer Daten jederzeit widersprechen. Das Datenhandling bei Sack Fachmedien erklären wir Ihnen in unserer Datenschutzerklärung.